Permanently elastic 25 % movement capability.
No shrinkage.
Cures bubble-free.
No sagging – Thixotropic.
Over paintable.
Suitable both for indoor and outdoor applications.
Suitable for light and medium traffic.
Strong adhesion on metal, glass, wood, concrete, brick, tile.

Sealing and bonding applications in vehicles.
In production and installment of vehicle bodies.
Elastic adhesion of wood, plasterboard, metal, brick, etc materials.
Sealing applications in static joints.
In roofing applications.
Joints between prefabricated construction materials.
Sealing and bonding of ventilation ducts, gutters, and spouts, etc.
Pre-cast concrete panels expansion joints.
Body construction of cars, containers, caravans, etc.
For vibration reduction in all types of sheet metal assembly works.

Shore A Hardness: 35-40

Density: 1,30 g/ml 

Tack-Free Time: 60 minutes 

Curing (24 hours): 2.5-3 mm 

Elongation at Break: >600 

Elastic Recovery: 1-1.20 MPa 

Shelf Life: 12 months 

Volume: 310 ml

Application surfaces must be clean and dry. Remove all dirt, oil grease, detergents, and loose material. Mask smooth surface to simplify clean up. Common construction materials do not need a primer application.
Cut the tip off the cartridge. Cut nozzle to the desired size at a 45°C angle. Insert the cartridge into a caulking gun. Push sealant ahead for a uniform bead. The joint width must be between 6-25mm. Tool within 15 minutes with a joint nail or putty knife. Clean off excess sealant with EMK or toluene before it gets dried.

It contains isocyanates and minor amounts of volatile organic chemicals. Since it may cause irritation to avoid prolonged contact of wet sealant to the skin and preferably use gloves.

Below +5°C, the extrusion and curing rates of PU sealant will decrease significantly.
Tends to become yellowish if constantly exposed to UV.